Use of martensitic stainless steel welding consumable to substantially improve the fatigue strength of low alloy steel welded structures
Créé le : 16/06/2014

Scandella F., Cavalin N., Gressel P., Haous J., Jubin L., Lefebvre F., Hutter I. - 01/09/2013 - www.iiwelding.org/sites/Commission-XIII/WUDocuments/XIII-2481www.iiwelding.org/sites/Commission-II/WUDocuments/II-1875

Ohta et al. have developed an iron base alloy containing 10 wt.% Cr and 10 wt.%Ni with a martensite start temperature around 180°C. Numerous studies have shown that Low γ → α’ Transformation Temperature (LTT) welding consumables enable weld beads to be in compression after cooling. Owing to this, fatigue strength can be substantially improved.